Auto Parts Heat Treatment Rapid Prototypes

Heat treatments can be applied to metal alloys throughout the manufacturing process. For CNC machined parts, heat treatments are typically applied either:
Before CNC machining: When a standardized grade of a metal alloy is requested that is readily available, the CNC service provider will machine the parts directly from that stock material. This is often the best option for reducing lead times.
After CNC machining: Some heat treatments significantly increase the hardness of the material or are used as a finishing step after forming. In these cases, the heat treatment is applied after CNC machining, as high hardness reduces the machinability of a material. For example, this is standard practice when CNC machining tool steel parts.The following is about Auto Parts Heat Treatment Rapid Prototypes.

Send Inquiry

Product Description

Auto Parts Heat Treatment Rapid Prototypes


Heat treatments can be applied to metal alloys throughout the manufacturing process. For CNC machined parts, heat treatments are typically applied either:

Before CNC machining: When a standardized grade of a metal alloy is requested that is readily available, the CNC service provider will machine the parts directly from that stock material. This is often the best option for reducing lead times.

After CNC machining: Some heat treatments significantly increase the hardness of the material or are used as a finishing step after forming. In these cases, the heat treatment is applied after CNC machining, as high hardness reduces the machinability of a material. For example, this is standard practice when CNC machining tool steel parts.

"Sincerity, Innovation, Rigorousness, and Efficiency" is the persistent conception of our firm for the long-term to create jointly with consumers for mutual reciprocity and mutual reward for Factory Cheap China High Precision Customized Auto Parts Heat Treatment Rapid Prototypes Manufacturers, We warmly welcome you to build cooperation and generate a brilliant long term together with us. Factory Cheap China Turning Parts, CNC Machining Parts, You can always find the products you require in our company! Welcome to inquire us about our product and anything we know and we can help in auto spare parts. We're looking forward to work with you for a win-win situation.

1.Product ParameterforAuto Parts Heat Treatment Rapid Prototypes


When you place a CNC order, there are three ways to request a heat treatment:

Give a reference to a manufacturing standard: Many heat treatments are standardized and widely used. For example, the T6 indicator in aluminum alloys (6061-T6, 7075-T6 and so on) shows that the material has been precipitation hardened.

Specify the required hardness: This is a common method of specifying a heat treatment for tool steels and case hardening. This will indicate to the manufacturer the heat treatment he needs to perform after CNC machining. For example, for D2 tool steel, it is common to request a hardness of 56-58 HRC.

Specify the heat treatment cycle: When the specifics of the required heat treatment are known, then these can be communicated to the supplier when placing the order. This way you can specifically modify the material properties for your application. Of course, this requires advanced metallurgical knowledge.

 

2.Product Feature forAuto Parts Heat Treatment Rapid Prototypes


 Youtube

Heat treatment

Purpose

Compatible materials

Annealing

To improve the machinability of the metal alloy

All metal alloys

Stress relieving

To release residual stresses from mechanical deformation or temperature increase during processing

All metal alloys

Tempering

To reduce brittleness after quenching

Mild steels (1045, A36)
Alloy steels (4140, 4240)
Tool steels (A2)

  

3.Product Details forAuto Parts Heat Treatment Rapid Prototypes


Heat treatments can be applied to many metal alloys to drastically improve key physical properties (for example hardness, strength or machinability). These changes happen due to modifications to the microstructure and, sometimes, the chemical composition of the material.

Those treatments involve the heating of the metal alloys to (usually) extreme temperatures, followed by a cooling step under controlled conditions. The temperature the material is heated to, the time it is kept at that temperature and the cooling rate all greatly affect the final physical properties of the metal alloy.



4.FAQ


Q1:Where can I get product&price information?

A1:Send us inquirye-mail, we will contact you as we receive your mail. 

Q2:How long can i get the sample?

A2:Depends on your specific items,within 3-7 days is required generally.

Q3:What's kinds of information you need for quote?

A3:Kindly please provide the product drawing in PDF,and will be better you can provde in STEP or IGS, send the parts materials, quantity, surface finishing and other requirements to us as well.

Q4: what's the payment terms?

A4: We accept 50% as payment deposit, when the goods is done, we take photoes for your check and you then pay the balance.

For small amount, we also accept Paypal, Paypal commission will be added to the order. For big amount, T/T is preferred

Q5.Are you a trading company or factory?

A5:We are direct factory with 10 experienced engineers and more than 30 employees as well approximate 3,000 square meters workshop area.

Q6. What shall we do if we do not have drawings?

Please send your sample to our factory,then we can copy or provide you better solutions. Please send us pictures or drafts with dimensions(Length,Hight,Width),CAD or 3D file will be made for you if placed order.

Q7. Can we get some samples before mass production?

A7:Absolutely

Q8. What is your MOQ?

Our MOQ is 1pcs, it is also our one of advantage, even you have less budget, or want to reduce the risks before production, we both can accept the less MOQ.

Q9: Will you do 100% inspection or random inspection ?

We will do 100% inspection for samples, random inspection for mass production. When manufacturing, we will control the dimensions , do PQC in mass production.

Q10. How to do if the parts not match with drawings we received?

Contact us immediately, send the pictures and tell us the issues, we will check and repair or re-make the goods with free.

Q11. You will how to ship the parts to me?

When products finished, also passed by our QC, we will ship out the parts to you by DHL, Fedex , or by sea after communication


6.Deliver,Shipping for Auto Parts Heat Treatment Rapid Prototypes



Hot Tags: Auto Parts Heat Treatment Rapid Prototypes, China, Suppliers, Manufacturers, Factory, Discount, Buy Discount, Low Price, Customized, Cheap, Quality, Newest, Durable, Latest Selling, Made in China

Related Category

Send Inquiry

Please feel free to give your inquiry in the form below. We will reply you within 24 hours.